ASTM |
Grade |
Classification |
CHEMICAL
COMPOSITION |
MECHANICAL
PROPERTIES |
C
% |
Mn
% |
P
Max
% |
S
Max
% |
Si
% |
Ni
% |
Cr
% |
Mo
% |
T.S
Min.psi
(kg/mm2) |
Y.S
Min.psi
(kg/mm2) |
EL
Min
% |
Red
Min
% |
HB |
A-105*
A-181
A-181
|
60
70
|
Carbon
Steel
Carbon
Steel
Carbon
Steel |
MAX
0.35
MAX
0.35
MAX
0.35 |
0.60-
1.05
MAX
0.90
MAX
0.90 |
0.040
0.050
0.050 |
0.050
0.050
0.050 |
MAX
0.35
MAX
(0.35)
MAX
(0.35) |
MAX
0.40 |
MAX
0.30 |
MAX
0.12 |
70.000
(49.2)
60.000
(42.2)
70.000
(49.2) |
36.000
(25.3)
30.000
(21.1)
35.000
(25.3) |
22
22
18 |
30
35
24 |
MAX
187 |
A-182
A-182
A-182
|
F1
F5
F5a |
1/2Mo
5Cr-1/2Mo
5Cr-1/2Mo |
MAX
0.28
MAX
0.15
MAX
0.25 |
0.60-
0.90
0.30-
0.60
MAX
0.6 |
0.045
0.030
0.040 |
0.045
0.030
0.030 |
0.15-
0.35
MAX
0.50
MAX
0.50 |
MAX
0.50
MAX
0.50 |
4.00-
6.00
4.00-
6.00 |
0.44-
0.65
0.44-
0.65
0.44-
0.65 |
70.000
(49.2)
70.000
(49.2)
90.000
(63.3) |
40.000
(28.1)
40.000
(28.1)
65.000
(45.7) |
20
20
22 |
30
35
50 |
143-
192
143-
217
187-
248 |
A-182
A-182
A-182
A-182
A-182
|
F11-1
F11-2
F12-1
F12-1
F12-2 |
11/4Cr-1/2Mo
1Cr-1/2Mo
1Cr-1/2Mo
1Cr-1/2Mo
1Cr-1/2Mo |
0.05-
0.15
0.10-
0.20
0.10-
0.20
0.05-
0.15
0.10-
0.20 |
0.30-
0.60
0.30-
0.80
0.30-
0.80
0.30-
0.60
0.30-
0.80 |
0.030
0.040
0.040
0.045
0.040 |
0.030
0.040
0.040
0.045
0.040 |
0.50-
1.00
0.50-
1.00
0.50-
1.00
MAX
0.50
0.10-
0.60 |
|
1.00-
1.50
1.00-
1.50
1.00-
1.50
0.80-
1.25
0.80-
1.25 |
0.44-
0.65
0.44-
0.65
0.44-
0.65
0.44-
0.65
0.44-
0.65 |
60.000
(42.2)
70.000
(49.2)
75.000
(52.7)
60.000
(42.2)
70.000
(49.2) |
30.000
(21.2)
40.000
(28.1)
45.000
(31.6)
30.000
(21.1)
40.000
(28.1) |
20
20
20
20
20 |
45
30
30
45
30 |
121-
174
143-
207
156-
207
121-
174
143-
207 |
A-182
A-182
A-182
|
F11
F12
F22
|
11/4Cr-1/2Mo
1Cr-1/2Mo
21/4Cr-1Mo |
0.10-
0.20
0.10-
0.20
MAX
0.15 |
0.30-
0.60
0.30-
0.80
0.30-
0.60 |
0.040
0.040
0.040 |
0.040
0.040
0.040 |
0.50-
1.00
0.10-
0.60
MAX
0.50 |
|
1.00-
1.50
0.80-
1.25
2.00-
2.50 |
0.44-
0.65
0.44-
0.65
0.87-
1.13 |
70.000
(49.2)
70.000
(49.2)
75.000
(52.7) |
40.000
(28.1)
40.000
(28.1)
45.000
(31.6) |
20
20
20 |
30
30
30 |
143-
207
143-
207
156-
207 |
A-182
A-182
A-182
|
F304
F304L
F316 |
18Cr-8Ni
18Cr-8Ni
low
18Cr-8Ni
Mo |
MAX
0.08
MAX
0.35
MAX
0.08 |
MAX
2.00
MAX
2.00
MAX
2.00 |
0.040
0.040
0.040 |
0.030
0.030
0.030 |
MAX
1.00
MAX
1.00
MAX
1.00 |
8.00-
11.00
8.00-
13.00
10.00-
14.00 |
18.00-
20.00
18.00-
20.00
16.00-
18.00 |
2.00-
3.00 |
75.000
(52.7)
70.000
(49.2)
75.000
(52.70 |
30.000
(21.1)
25.000
(17.6)
30.000
(21.7) |
30
30
30 |
50
50
50 |
|
A-182
A-182
A-182
|
F316L
F321
F347 |
18Cr-8Ni
Mo-low
18Cr-8Ni
Ti
18Cr-8Ni Cb |
MAX
0.035
MAX
0.08
MAX
0.08 |
MAX
2.00
MAX
2.00
MAX
2.00 |
0.040
0.030
0.030 |
0.030
0.030
0.030 |
MAX
1.00
MAX
1.00
MAX
1.00 |
10.00-
15.00
9.00-
12.00
9.00-
13.00 |
16.00-
18.00
Min
17.00
17.00-
20.00 |
2.00-
3.00 |
65.000
(45.7)
75.000
(52.7)
75.000
(52.7) |
25.000
(17.6)
30.000
(21.1)
30.000
(21.1) |
30
30
30 |
50
50
50 |
|
A-350*
A-350*
A-350*
|
LF1
LF2
LF3 |
Carbon
Steel
Carbon
Steel
31/2 Ni |
MAX
0.30
MAX
0.30
MAX
0.20 |
0.75-
1.05
MAX
1.35
MAX
0.90 |
0.035
0.035
0.035 |
0.040
0.040
0.040 |
0.15-
0.30
0.15-
0.30
0.20-
0.35 |
MAX
0.40
MAX
0.40
3.25-
3.75 |
MAX
0.12
MAX
0.12
MAX
0.12 |
MAX
0.12
MAX
0.12
MAX
0.12 |
60.000-85.000
(42.5-59.7)
70.000-95.000
(49.2-66.8)
70.000-95.000
(49.2-66.8) |
30.000
(21.1)
36.000
(25.3)
37.500
(26.4) |
25
22
22 |
38
30
35 |
|