OTHER IMPORTANT
BASIC REFRACORY BRICKS MAGNESITE
BRICK
|
With
good slag resistance, high refractoriness, its physical property
is better, used in open-hearth furnace, oxygen converters,
electric arc furnace, torpedo, and the basis zone of non-ferrous
metal furnaces. The high-quality magnesite brick is also suitable
to the special zones of hot-work equipments in the alkaline
medium environment. |
|
|
Index
Item
|
Magnesia brick |
High quality magnesia brick |
MZ-91 |
MZ-89 |
MZ-87 |
LMZ-95 |
LMZ-93 |
MgO % ¡Ý |
91 |
89 |
87 |
94.5 |
93 |
CaO % ¡Ü |
3 |
3 |
3 |
2.0 |
2.0 |
SiO2 % ¡Ü |
|
|
|
2.5 |
3.5 |
Refractoriness under ¡æ¡Ý |
1550 |
1540 |
1520 |
1650 |
1620 |
A.P. % ¡Ü |
18 |
20 |
20 |
18 |
17 |
C.C.S (Mpa) ¡Ý |
58.8 |
49 |
39.2 |
50 |
65 |
Linear change after reheating %(1650x2h)
|
0-0.5 |
0-0.6 |
0-0.6 |
0-0.4 |
|
MAGNESIA-ALUMINA
BRICK
|
The
Magnesia-Alumina brick has higher temperature strength, good
thermal shock stability, and strong resistance to basic slag. |
|
|
Index
Item |
Magnesia-alumina brick for open hearth
furnaces roof |
MI-80A |
ML-80B |
MgO % ¡Ý |
80 |
80 |
Al2O3 % |
5-10 |
5-10 |
SiO2 % ¡Ý |
|
|
Refractoriness under ¡æ¡Ý |
1600 |
1580 |
A.P. % ¡Ü |
18 |
20 |
C.C.S (Mpa) ¡Ý |
39.2 |
39.4 |
|
|
|
The
product is a basic refractory with the advantages of high temperature
constructural strength, excellent thermal stability, high refractoriness,
and strong resistance to basic material.
Magnesia-chrome
brick is extensively appreciated in non-ferrous furnace,electric
arc furnace, open hearth furnace, converter, torpedo, vacuum
refining furnace, burning zone of cement rotary kiln, recuperator
of glass kiln. |
|
Item
Index
|
MgO%
¡Ý |
Cr2O3
¡Ý |
SiO2%
¡Ý |
Apparent porosity
¡Ü |
Refractoriess under
¡æ¡Ý |
Cold rushing
Strength
¡Ý |
Magnesia-chrome bricks |
Mge -20 |
40 |
20 |
|
23 |
1550 |
24.5 |
Mge-16 |
45 |
16 |
|
23 |
1550 |
24.5 |
Mge-12 |
55 |
12 |
|
23 |
1550 |
24.5 |
Mge-8 |
60 |
8 |
|
24 |
1530 |
24.5 |
Externol plating unfired magnesia chrone
bricks |
LTMGe-12A |
50 |
12 |
|
16 |
1500 |
34 |
LTMGe-12B |
63 |
12 |
|
23 |
1500 |
25 |
LTMGe-16 |
45 |
16 |
|
16 |
1500 |
34 |
Direct-bonded magnesia chrome bricks |
LZMGe-8A |
70 |
8 |
1.5 |
18 |
1700 |
40 |
LZMGe-8B |
|
8 |
2.5 |
18 |
1700 |
40 |
LZMGe-8C |
|
8 |
3.0 |
19 |
1650 |
40 |
LZMGe-8D |
|
8 |
4.0 |
21 |
1550 |
30 |
LZMGe-12A |
65 |
12 |
1.5 |
18 |
1700 |
40 |
LZMGe-12B |
|
12 |
2.5 |
18 |
1700 |
40 |
LZMGe-12C |
|
12 |
3.0 |
18 |
1650 |
40 |
LZMGe-16A |
|
16 |
1.5 |
18 |
1700 |
40 |
LZMGe-16B |
|
16 |
2.5 |
18 |
1700 |
40 |
LZMGe-18 |
55 |
18 |
1.5 |
18 |
1700 |
40 |
LZMGe-18A |
|
18 |
1.5 |
18 |
1700 |
40 |
LZMGe-18B |
|
18 |
2.5 |
18 |
1700 |
40 |
DMC-12 |
60 |
12 |
3.2 |
19 |
1580 |
35 |
DMC-9A |
70 |
9 |
3.0 |
19 |
1580 |
40 |
DMC-9B |
70 |
9 |
2.8 |
19 |
1600 |
40 |
DMC-6 |
75 |
6 |
2.8 |
18 |
1600 |
40 |
DMC-4 |
80 |
4 |
2.5 |
18 |
1600 |
40 |
LZGeM-20 |
58 |
20 |
1.5 |
18 |
1700 |
35 |
LZGeM-26 |
45 |
26 |
|
21 |
1700 |
35 |
Semi-rebounded magnesia chrome bricks |
LBMGe-16A |
55 |
16 |
2.5 |
16 |
1700 |
35 |
LBMGe-16B |
55 |
16 |
3.5 |
16 |
1690 |
35 |
LBMGe-18A |
50 |
18 |
2.5 |
19 |
1700 |
50 |
LBMGe-20A |
50 |
20 |
2.5 |
16 |
1700 |
35 |
LBMGe-20B |
50 |
20 |
3.45 |
16 |
1690 |
35 |
Fully co-clinker rebounded magnesia chrome
bricks |
LQMGe-12 |
60 |
12 |
2.5 |
18 |
1700 |
30 |
LQMGe-18 |
52 |
18 |
2.5 |
18 |
1700 |
30 |
LQMGe-20 |
50 |
20 |
2.5 |
18 |
1700 |
30 |
Fused rebounded magnesia chrome bricks |
LDMGe-12A |
60 |
12 |
2.5 |
16 |
1700 |
35 |
LDMGe-12B |
60 |
12 |
3.5 |
16 |
1700 |
35 |
LDMGe-14 |
60 |
12 |
2.5 |
16 |
1700 |
40 |
LDMGe-16A |
55 |
16 |
2.5 |
16 |
1700 |
35 |
LDMGe-16B |
55 |
16 |
3.5 |
17 |
1700 |
35 |
LDMGe-18 |
55 |
18 |
2.5 |
16 |
1700 |
35 |
LDMGe-20 |
50 |
20 |
2.5 |
|
|
|
Fused rebounded magnesia |
LDM-97 |
97 |
|
1.5 |
18 |
1700 |
45 |
LDM-95 |
95 |
|
2.0 |
18 |
1700 |
45 |
|
|
|
MAGNESIA-Dolomite-Carbon
Bricks
Item
Index |
Al2O3
(%) |
MgO
(%)¡Ý |
C
(%) |
A.P.
(%) |
B.D.
(g/cm3) |
C.C.S.
(Mpa) |
Refrctoriness under load ¡Ý |
LMGT68 |
8-12 |
68 |
8-13 |
4 |
¡¡ |
25 |
1700 |
|